Professional Poly Ether Ether Ketone PEEK Material and PEEK Fiber Manufacturer in China

Carbon Fiber Reinforced PEEK factory

Product Name:Carbon Fiber Reinforced PEEK 
Synonyms: 4,4’-Difluorobenzophenone,hydroquinonepolymer;CF PEEK 
CAS No.:29658-26-2;31694-16-3 
Property:Polyether ether ketone (PEEK) is a colourless organic thermoplastic polymer in the polyaryletherketone (PAEK) family, used in engineering applications.
Applications The Carbon Fiber Reinforced PEEK can be used the processing method such as extrusion molding and injection Molding.

Type: CF7030

Index
Standard
Test condition
Unit
Index
Tensile strength
ISO527
23℃
Mpa
260
Elongation
ISO527
23℃
%
1.5-2
Bending strength
ISO178
23℃
Mpa
380
Mold Shrinkage
ISO294-1
Parallel to the direction of flow
%
0.1
Perpendicular to the direction of flow
0.5
Melting point
ISO11357
 
343
Glass transition temperature
ISO11357
143
Thermal conductivity
ISO22007-4
23℃
w m-1 k-1
0.95
Heat distortion temperature
ISO75-f
1.8MPa
336
Specific heat capacity
DSC
23℃
KJ kg-1 ℃-1
1.8
Melt flow index
ISO11443
380℃ , 5kg
g 10min-1
2.3
Density
ISO1183
crystallization
g cm-3
1.4
non-crystalline
Shore Hardness
ISO868
23℃
85-90

Type: CF7020
Index
Standard
Test condition
Unit
Index
Tensile strength
ISO527
23℃
Mpa
210
Elongation
ISO527
23℃
%
1.5-2
Bending strength
ISO178
23℃
Mpa
310
Mold Shrinkage
ISO294-1
Parallel to the direction of flow
%
0.2
Perpendicular to the direction of flow
0.7
Melting point
ISO11357
 
343
Glass transition temperature
ISO11357
143
Thermal conductivity
ISO22007-4
23℃
w m-1 k-1
0.95
Heat distortion temperature
ISO75-f
1.8MPa
325
Specific heat capacity
DSC
23℃
KJ kg-1 ℃-1
1.8
Melt flow index
ISO11443
380℃ , 5kg
g 10min-1
4
Density
ISO1183
crystallization
g cm-3
1.27
non-crystalline
Shore Hardness
ISO868
23℃
85-90

Type: CF5030
Index
Standard
Test condition
Unit
Index
Tensile strength
ISO527
23℃
Mpa
250
Elongation
ISO527
23℃
%
1.5-2
Bending strength
ISO178
23℃
Mpa
370
Mold Shrinkage
ISO294-1
Parallel to the direction of flow
%
0.1
Perpendicular to the direction of flow
0.5
Melting point
ISO11357
 
343
Glass transition temperature
ISO11357
143
Thermal conductivity
ISO22007-4
23℃
w m-1 k-1
0.95
Heat distortion temperature
ISO75-f
1.8MPa
336
Specific heat capacity
DSC
23℃
KJ kg-1 ℃-1
1.8
Melt flow index
ISO11443
380℃ , 5kg
g 10min-1
5
Density
ISO1183
crystallization
g cm-3
1.4
non-crystalline
Shore Hardness
ISO868
23℃
85-90

Type: CF5020
Index
Standard
Test condition
Unit
Index
Tensile strength
ISO527
23℃
Mpa
205
Elongation
ISO527
23℃
%
1.5-2
Bending strength
ISO178
23℃
Mpa
310
Mold Shrinkage
ISO294-1
Parallel to the direction of flow
%
0.2
Perpendicular to the direction of flow
0.7
Melting point
ISO11357
 
343
Glass transition temperature
ISO11357
143
Thermal conductivity
ISO22007-4
23℃
w m-1 k-1
0.95
Heat distortion temperature
ISO75-f
1.8MPa
325
Specific heat capacity
DSC
23℃
KJ kg-1 ℃-1
1.8
Melt flow index
ISO11443
380℃ , 5kg
g 10min-1
7
Density
ISO1183
crystallization
g cm-3
1.37
non-crystalline
Shore Hardness
ISO868
23℃
85-90

Type:CF3030
Index
Standard
Test condition
Unit
Index
Tensile strength
ISO527
23℃
Mpa
250
Elongation
ISO527
23℃
%
1.5-2
Bending strength
ISO178
23℃
Mpa
360
Mold Shrinkage
ISO294-1
Parallel to the direction of flow
%
0.1
Perpendicular to the direction of flow
0.5
Melting point
ISO11357
 
343
Glass transition temperature
ISO11357
143
Thermal conductivity
ISO22007-4
23℃
w m-1 k-1
0.95
Heat distortion temperature
ISO75-f
1.8MPa
339
Specific heat capacity
DSC
23℃
KJ kg-1 ℃-1
1.8
Melt flow index
ISO11443
380℃ , 5kg
g 10min-1
27
Density
ISO1183
crystallization
g cm-3
1.4
non-crystalline
Shore Hardness
ISO868
23℃
85-90

Type: P3025
Index
Standard
Test condition
Unit
Index
Tensile strength
ISO527
23℃
Mpa
250
Elongation
ISO527
23℃
%
1.5-2
Bending strength
ISO178
23℃
Mpa
360
Mold Shrinkage
ISO294-1
Parallel to the direction of flow
%
0.2
Perpendicular to the direction of flow
0.7
Melting point
ISO11357
 
343
Glass transition temperature
ISO11357
143
Thermal conductivity
ISO22007-4
23℃
w m-1 k-1
0.95
Heat distortion temperature
ISO75-f
1.8MPa
339
Specific heat capacity
DSC
23℃
KJ kg-1 ℃-1
1.8
Melt flow index
ISO11443
380℃ , 5kg
g 10min-1
27
Density
ISO1183
crystallization
g cm-3
1.4
non-crystalline
Shore Hardness
ISO868
23℃
85-90




Our Mission

Continuously provide the Poly EtherEther Ketone(PEEK),Polyphenylene Sulfone(PPSU) and Polyethersulfone(PES) with lower energy consumption and excellent performance for Industries
Continuously improve the technology of environmentally friendly

Contact Us

 Dongfeng EastStreet, Weifang Shandong China

 (0086) 536-8216-345