Product Name:Wearproof PEEK
Synonyms: 4,4’-Difluorobenzophenone,hydroquinonepolymer;Wearproof PEEK
CAS No.:29658-26-2;31694-16-3
Property:Polyether ether ketone (PEEK) is a colourless organic thermoplastic polymer in the polyaryletherketone (PAEK) family, used in engineering applications.
Applications: The Wearproof PEEK is 10% PTFE + 10% carbon fiber + 10% graphite reinforced, it can be used the processing method such as extrusion molding and injection Molding.
Type: WP7030
Index |
Standard |
Test condition |
Unit |
Index |
Tensile strength |
ISO527 |
23℃ |
Mpa |
140 |
Elongation |
ISO527 |
23℃ |
% |
2-2.5 |
Bending strength |
ISO178 |
23℃ |
Mpa |
230 |
Mold Shrinkage |
ISO294-1 |
Parallel to the direction of flow |
% |
0.3 |
Perpendicular to the direction of flow |
0.7 |
|||
Melting point |
ISO11357 |
℃ |
343 |
|
Glass transition temperature |
ISO11357 |
℃ |
143 |
|
Thermal conductivity |
ISO22007-4 |
23℃ |
w m-1 k-1 |
0.87 |
Heat distortion temperature |
ISO75-f |
1.8MPa |
℃ |
315 |
Specific heat capacity |
DSC |
23℃ |
KJ kg-1 ℃-1 |
1.8 |
Melt flow index |
ISO11443 |
380℃ , 5kg |
g 10min-1 |
2.5 |
Density |
ISO1183 |
crystallization |
g cm-3 |
1.45 |
non-crystalline |
||||
Shore Hardness |
ISO868 |
23℃ |
80-85 |
Type:WP3030
Index |
Standard |
Test condition |
Unit |
Index |
Tensile strength |
ISO527 |
23℃ |
Mpa |
140 |
Elongation |
ISO527 |
23℃ |
% |
2-2.5 |
Bending strength |
ISO178 |
23℃ |
Mpa |
230 |
Mold Shrinkage |
ISO294-1 |
Parallel to the direction of flow |
% |
0.3 |
Perpendicular to the direction of flow |
0.7 |
|||
Melting point |
ISO11357 |
℃ |
343 |
|
Glass transition temperature |
ISO11357 |
℃ |
143 |
|
Thermal conductivity |
ISO22007-4 |
23℃ |
w m-1 k-1 |
0.87 |
Heat distortion temperature |
ISO75-f |
1.8MPa |
℃ |
315 |
Specific heat capacity |
DSC |
23℃ |
KJ kg-1 ℃-1 |
1.8 |
Melt flow index |
ISO11443 |
380℃ , 5kg |
g 10min-1 |
2.5 |
Density |
ISO1183 |
crystallization |
g cm-3 |
1.4 |
non-crystalline |
||||
Shore Hardness |
ISO868 |
23℃ |
80=85 |