Glass Fiber Reinforced PEEK factory

Product Name:Glass Fiber Reinforced PEEK 
Synonyms: 4,4’-Difluorobenzophenone,hydroquinonepolymer;GF PEEK 
CAS No.:29658-26-2;31694-16-3 
Property:Polyether ether ketone (PEEK) is a colourless organic thermoplastic polymer in the polyaryletherketone (PAEK) family, used in engineering applications.
Applications The Glass Fiber Reinforced PEEK can be used the processing method such as extrusion molding and injection Molding.

Type: GF7030

Index
Standard
Test condition
Unit
Index
Tensile strength
ISO527
23℃
Mpa
175
Elongation
ISO527
23℃
%
2-3
Mold Shrinkage
ISO294-1
Parallel to the direction of flow
%
0.3
Perpendicular to the direction of flow
0.8
Melting point
ISO11357
 
343
Glass transition temperature
ISO11357
143
Thermal conductivity
ISO22007-4
23℃
w m-1 k-1
0.3
Heat distortion temperature
ISO75-f
1.8MPa
328
Specific heat capacity
DSC
23℃
KJ kg-1 ℃-1
1.7
Melt flow index
ISO11443
380℃ , 5kg
g 10min-1
4.5
Density
ISO1183
crystallization
g cm-3
1.51
non-crystalline
Shore Hardness
ISO868
23℃
85-90
Dielectric strength
IEC60243
2MM
kv mm-1
25
Dielectric constant
IEC60250
23℃ 1kHz
3.2
Loss tangent
IEC60250
23℃ 1MHz
0.005

Type: GF7020
Index
Standard
Test condition
Unit
Index
Tensile strength
ISO527
23℃
Mpa
155
Elongation
ISO527
23℃
%
3-4
Mold Shrinkage
ISO294-1
Parallel to the direction of flow
%
0.3
Perpendicular to the direction of flow
0.8
Melting point
ISO11357
 
343
Glass transition temperature
ISO11357
143
Thermal conductivity
ISO22007-4
23℃
w m-1 k-1
0.3
Heat distortion temperature
ISO75-f
1.8MPa
315
Specific heat capacity
DSC
23℃
KJ kg-1 ℃-1
1.7
Melt flow index
ISO11443
380℃ , 5kg
g 10min-1
6.5
Density
ISO1183
crystallization
g cm-3
1.51
non-crystalline
Shore Hardness
ISO868
23℃
85-90
Dielectric strength
IEC60243
2MM
kv mm-1
24
Dielectric constant
IEC60250
23℃ 1kHz
3.1
Loss tangent
IEC60250
23℃ 1MHz
0.005

Type: GF5030
Index
Standard
Test condition
Unit
Index
Tensile strength
ISO527
23℃
Mpa
175
Elongation
ISO527
23℃
%
2-3
Mold Shrinkage
ISO294-1
Parallel to the direction of flow
%
0.3
Perpendicular to the direction of flow
0.8
Melting point
ISO11357
 
343
Glass transition temperature
ISO11357
143
Thermal conductivity
ISO22007-4
23℃
w m-1 k-1
0.3
Heat distortion temperature
ISO75-f
1.8MPa
328
Specific heat capacity
DSC
23℃
KJ kg-1 ℃-1
1.7
Melt flow index
ISO11443
380℃ , 5kg
g 10min-1
6
Density
ISO1183
crystallization
g cm-3
1.51
non-crystalline
Shore Hardness
ISO868
23℃
85-90
Dielectric strength
IEC60243
2MM
kv mm-1
25
Dielectric constant
IEC60250
23℃ 1kHz
3.2
Loss tangent
IEC60250
23℃ 1MHz
0.005

Type: GF5020
Index
Standard
Test condition
Unit
Index
Tensile strength
ISO527
23℃
Mpa
155
Elongation
ISO527
23℃
%
3-4
Mold Shrinkage
ISO294-1
Parallel to the direction of flow
%
0.3
Perpendicular to the direction of flow
0.8
Melting point
ISO11357
 
343
Glass transition temperature
ISO11357
143
Thermal conductivity
ISO22007-4
23℃
w m-1 k-1
0.3
Heat distortion temperature
ISO75-f
1.8MPa
315
Specific heat capacity
DSC
23℃
KJ kg-1 ℃-1
1.7
Melt flow index
ISO11443
380℃ , 5kg
g 10min-1
11
Density
ISO1183
crystallization
g cm-3
1.51
non-crystalline
Shore Hardness
ISO868
23℃
85-90
Dielectric strength
IEC60243
2MM
kv mm-1
24
Dielectric constant
IEC60250
23℃ 1kHz
3.1
Loss tangent
IEC60250
23℃ 1MHz
0.005

Type: GF3030
Index
Standard
Test condition
Unit
Index
Tensile strength
ISO527
23℃
Mpa
185
Elongation
ISO527
23℃
%
2-3
Mold Shrinkage
ISO294-1
Parallel to the direction of flow
%
0.3
Perpendicular to the direction of flow
0.8
Melting point
ISO11357
 
343
Glass transition temperature
ISO11357
143
Thermal conductivity
ISO22007-4
23℃
w m-1 k-1
0.3
Heat distortion temperature
ISO75-f
1.8MPa
335
Specific heat capacity
DSC
23℃
KJ kg-1 ℃-1
1.7
Melt flow index
ISO11443
380℃ , 5kg
g 10min-1
28
Density
ISO1183
crystallization
g cm-3
1.51
non-crystalline
Shore Hardness
ISO868
23℃
85-90
Dielectric strength
IEC60243
2MM
kv mm-1
23
Dielectric constant
IEC60250
23℃ 1kHz
3.3
Loss tangent
IEC60250
23℃ 1MHz
0.005

Type: GF3020
Index
Standard
Test condition
Unit
Index
Tensile strength
ISO527
23℃
Mpa
145
Elongation
ISO527
23℃
%
2-3
Mold Shrinkage
ISO294-1
Parallel to the direction of flow
%
0.3
Perpendicular to the direction of flow
0.8
Melting point
ISO11357
 
343
Glass transition temperature
ISO11357
143
Thermal conductivity
ISO22007-4
23℃
w m-1 k-1
0.3
Heat distortion temperature
ISO75-f
1.8MPa
323
Specific heat capacity
DSC
23℃
KJ kg-1 ℃-1
1.7
Melt flow index
ISO11443
380℃ , 5kg
g 10min-1
40
Density
ISO1183
crystallization
g cm-3
1.51
non-crystalline
Shore Hardness
ISO868
23℃
85-90
Dielectric strength
IEC60243
2MM
kv mm-1
23
Dielectric constant
IEC60250
23℃ 1kHz
3.2
Loss tangent
IEC60250
23℃ 1MHz
0.004

 




Our Mission

Continuously provide the Poly EtherEther Ketone(PEEK),Polyphenylene Sulfone(PPSU) and Polyethersulfone(PES) with lower energy consumption and excellent performance for Industries
Continuously improve the technology of environmentally friendly

Contact Us

 Dongfeng EastStreet, Weifang Shandong China

 (0086) 536-8216-345